Partial Addition of Lime in Mortar

Project Description:

Addition of lime to cement is kept partial for enhancing the strength by using a different dosage of natural admixtures and the main aim is to reduce the emission of CO2. Natural admixtures varied from 10% to 50%.
1. Lime: Lime is produced by heating limestone which is more or less pure calcium carbonate. During heating, carbon-dioxide is driven off and non-volatile impurities such as oxides of silicon, magnesium, aluminum, iron, and manganese are left behind in the lime.
2. Cement:Hydraulic cement, more commonly known as cement, is one of the most basic binding material in almost all civil engineering constructions. The term cement is restricted to the bonding materials used with stones, sand, bricks, building blocks etc., which are used in constructions. The compounds of lime are the principal constituents of this type of cement so that in building in civil engineering we are considered with the calcareous cement. The cement is used in making of concrete which has the property of setting and also used in underwater by good qualities of a chemical reaction with it.
3. Jaggery:Jaggery water was used as a natural admixture at the ancient constructions for its good binding properties. Jaggery water is gathered from the palm tree and it has dark brown color. It makes the structure thermally insulated. It has a complex structure combined with sucrose, invert sugar, moisture, and other insoluble matter, like wood ash, proteins, and fibers.
4. Kadukkai: It has extraordinary binding and hardened properties. Kadukkai can be used in construction only after it is made into a dried powder form for its effective usage. The dried kadukkai powder is mixed with sufficient water and enclosed for three days for making kadukkai paste. This paste is used for the mortar preparation.

Project Implementation:

1. Mixing Proportions:For this experiment take 1:3 proportion and is the rich mortar ratio. Jaggery and Kadukkai.
2. Mixture: Natural admixture like jaggery, water and kadukkai paste mixed with water. 50% of the cement was replaced by the hydrated lime powder and mixed with fine aggregates and water.
3. Casting: Fresh mortars should be cast into 70.6mm cube moulds for compression testing and must be removed after 48 hours.
4. Curing: Specimens are removed from the mould and kept in water for 7-28 days.
5. Repeat the above steps forproportion from 10-50% of lime-cement mortar.